Título : REFORMADO DE METANO CON CO2 Y O2, SOBRE CATALIZADORES METÁLICOS ESTRUCTURADOS BASADOS EN PEROVSKITAS La1-YCeYCo1-XFeXO3
Otros títulos : STRUCTURED METAL CATALYSTS BASED ON PEROVSKITE La1-YCeYCo1-XFeXO3 FOR METHANE REFORMING WITH CO2 AND O2
Autor : García, Adriana Lucía
García, Luis
Goldwasser, Mireya
López, Carmen
Palabras clave : perovskitas;
gas de síntesis
reformado de metano
catalizadores estructurados; ;
Fecha de publicación : 10-Mar-2014
Citación : Revista Avances en Ciencias e Ingenieria;Volumen 2 n°2
http://www.exeedu.com/publishing.cl/av_cienc_ing/;
Resumen : Se prepararon catalizadores metálicos estructurados constituidos por perovskitas con composiciones LaCo0.6Fe0.4O3, LaCo0.4Fe0.6O3 y La0.9Ce0.1Co0.6Fe0.4O3 soportadas sobre estructuras cónicas de una malla de acero inoxidable 316, a fin de estudiar el efecto de la estructura metálica en la reacción. Estos catalizadores fueron evaluados en el reformado de metano con CO2 y O2, realizando la comparación con el sólido en polvo. Las condiciones de reacción fueron seleccionadas a partir de barridos de temperatura de reacción y de relación CH4/CO2 de la alimentación. Se alcanzó una conversión máxima de 88% y relación H2/CO de 1.6, para la perovskita de mayor contenido de Co a 850 °C y composición molar 6/1/3 en CH4/CO2/O2. Los catalizadores estructurados en forma de cono y en polvo presentaron un comportamiento similar. La sustitución de La por Ce no generó diferencias apreciables en el comportamiento catalítico. El uso de una estructura metálica similar a un empaque comercial, parece mejorar la estabilidad del catalizador LaCo0.6Fe0.4O3 con una mayor relación H2/CO en los productos.
Descripción : Perovskites with the compositions LaCo0.6Fe0.4O3, LaCo0.4Fe0.6O3 and La0.9Ce0.1Co0.6Fe0.4O3, were supported over metallic conic structures made of stainless steel, with the aim of study the influence of the metallic structure in the reaction. These catalysts were evaluated in methane reforming with CO2-O2, by comparing with the same catalyst in powder. The reactions conditions were established by modifying reaction temperature and CH4/CO2feed ratio. With the perovskite of higher cobalt content, at 850 ºC and molar composition 6/1/3 as CH4/CO2/O2, it was achieved a methane conversion of 88% and a ratio H2/CO of 1.6. A similar behavior was observed for the metal conic structured catalysts and powder catalysts. The substitution of La by Ce does not produce appreciable differences in catalytic behavior. Tests with a metallic structure similar to a commercial package seem to upgrade catalytic stability of LaCo0.6Fe0.4O3 perovskite, achieving a higher H2/CO ratio in the products
URI : http://saber.ucv.ve/jspui/handle/123456789/5748
ISSN : 0718-8706
Aparece en las colecciones: Artículos Publicados

Ficheros en este ítem:

Fichero Descripción Tamaño Formato
3-ACI1041-10-full.pdf663.15 kBAdobe PDFVisualizar/Abrir

Los ítems de DSpace están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.

 

Valid XHTML 1.0! DSpace Software Copyright © 2002-2008 MIT and Hewlett-Packard - Comentarios